Art of continuous galvanizing



June 1934- J. L. SCHUELER ART OF CONTINUOUS GALVANIZING o igi l Filed March '7, 1932 4 Sheets-Sheet l June 12, 1934. J. SCHUELER I ART OF CONTINUOUS GALVANIZING 4 Sheetsheet 2 Original Filed March 7, 1932 @Zz'azil. fic/zzzeZer June 12, 1934- J. 1.. SCHUELER I ART OF CONTINUOUS GALVANIZING Original Filed March '7, 1932 4 Sheets-Sheet 3 JZzZL'anL. 56/242816] qy I.

June 12, 1934.

J. L. SCHUELER Re. 19,209 ART OF CONTINUOUS GALVANIZING Original Filed Qh 1932 4 Sheets-Sheet 4 j H 0- \fLlL'arz/l5tfazeler Reissued June 12, 1934 19,209 ART OF CONTINUOUS GALVANIZING Julian L. Schueler, Kokomo, Ind.

Original No. 1,936,487, dated November 21, 1933, Serial No. 597,151, March 7, 1932. Application for reissue January 24, 1934, Serial No. 708,167

invention relates to a continuous process of coating iron and steel materials. It is applicable particularly to the coating of wiresuch v as is used for woven wire fence, barb wires, and the like. In the ensuing description, theinvention will be explained with reference to wire coated with zinc, by way of example, although I possibly it may be used to advantage with coatings other than zinc applied to iron and steel materials of different form It is a primary object of my invention to galvanize iron or steel wire by an improved proces in which the fluidity of the molten. zinc coating bath is controlled, in which the amount of coating carried by the wirefrom the bath is regulated, and in which the coating on the wire is uniformly distributed and smoothed by the action of flames which are directed upon every portion of the wire surface for a suitable interval of time. All of these operations are performed continuously and in immediate sequence. To carry out this process, I have found it advantageous to employ some such apparatus as is illustrated in the accompanying drawings 'in the manner following: V

Figure 1 is a side elevation of a'flame apparatus through which a number of wires travel in parallelism immediately, upon leaving the coating bath; the lower deflector surface of the apparatus is shown in vertical section to better illustrate the construction;

Fig. 2 which shows in side elevation the flame apparatus exhibits also at one end thereof an associated galvanizing bath and coating regulator,

5 and at the opposite end a guide by which to maintain the wires in proper position within the flame appa atus! Pg. 2 represents diagrammatically a transverse section through a galvanizing bath equipped 0 with means for accurately controlling the temperature of the molten metal therein;

Fig. 3 is an enlarged detail in vertical section showing the receiving end of the flame apparatus;

Fig. 4 is a similar View of the exit end of the flame apparatus;

Fig. 5 is a .detail in transverse vertical section on line 5 of Fig. 3;

Fig. 6 is a. fragmentary perspective view looking toward the rear side-of flame projector blocks positioned at the receiving end of the flame apparatus; I

- Fig. 7 is a detail in vertical section showing the coating regulator which ismounted at the exit end of the galvanizing bath;

Fig. 8 is a fragmentary view in transverse sec- 26 Claims. (01. 91-121) tion taken on line 8 of Fig. .7, showing in elevation the coating regulator in .relation to several wires; 1

Fig. 9 is a fragmentary detail on an enlarged scale showing certain of the coating regulator no parts;

Fig. 10 is a transverse vertical section through a flame apparatus of modified construction;

Fig. 11 is a similar view showing a further modification of the flame apparatus;

Fig. 12 shows also, in transverse section on line 12 of Fig. 13, one additional modification of the flame apparatus; and 7 Fig. 13 is an enlarged detail in vertical section taken on line 13 of Fig. 12. v e 7 In galvanizing wires according to this invention, it will be found desirable to utilize an annealing furnace, a cooling zone, an acid bath,

a water bath, a flux bath, a drier, and a molten zinc galvanizing bath, all as is common practice{ Up to the time the wires enter the molten coating bath, they need be subjected to onlythe usual processes. From this point on, however, the treatment involves a radical, departure.

First of all, I aim to maintain the coating bath at a uniform fluidity. Immediately upon emerging from the coating bath, the coating "upon the wire is regulated as to thickness by means which is automatic. and self-adjusting. Accordingly the amount of coating carried out of the molten bath by the wire is definitely "limited. In order that the coating so remaining on the wire may be uniformly distributed and made smooth and even, I subject the wire, immediately upon passing the regulator, to theaction of flames which. produce a redistribution of the-coating as necessary for complete uniformity and smoothness. In this manner, I .eliminate all rough points and cover all pin holes and'other bare spots. The work performed on the wire from the initial treatment in the annealing furnace, clear through the several units, including the flame apparatus, continues uninterruptedly and irrespective of joints between connected ends of wire bundles. All these operations take place with aminimum of attention while a plurality of wires are traveling at comparatively high speed, so that the process is economical to perform. 1

I have ascertained that there is a practicallimit to the amount of coating that can be evenly distributed around a wire and smoothed bya given amount of flame. It is desirable that all coating beyond that which can be acted upon by a flame should be removed in'advance by the coating regulator, leaving only a definite maxitravel which is economically necessary for galvanizing. The regulator employed fits more or wire, the same as is the notched bar, rests against the forward side of the latter so as to be movable away from the notched bar against the tension of the spring 34. This pivotal movement of the 5 less closely around the wire, with provision for lever 30, with consequent separation of the blade from the notched bar, may take place whenever 1 opening to allow joints to pass through. The fit of the regulator around the wire is determined with reference to speed of the wire under treatment, the length of its immersion in the molten coating bath, the fluidity of the molten metal itself, and perhaps other factors as well. According to this invention, all such factors should be accurately controlled for best results. The fluidity of the molten coating bath is a function of temperature, but as no suitable molten metal viscosimeter is available for routine testing, I maintain an even viscosity of the molten coating bath by controlling the temperature, plus or minus 5 Fahrenheit. This is accomplished by means of a temperature controller, set to maintain the heat in the bath at a desired point.

Referring now to the drawings, I have shown a bath A adapted to maintain zinc in a molten condition at a controlled temperature. A wire to leaving the'bath passes through a coating regulator R. which is desirably mounted adjacent the exit end thereof. The receiving end of the flame apparatus F is located close to the coating regulator so as to receive the wire while the coating is still in a fluid condition. Beyond the exit end of the flame apparatus is a guide G over which the wire travels before passing on through an air cooling space preliminary to being wound upon a reel. In practice, a large number of wires, perhaps thirty or more, are arranged to travel in parallelism through the galvanizing bath, the coating regulator, the flame apparatus, and over the guide, but for convenience in description I shall refer to a single wire, except only in connec tion with certain of the parts which are common to two or more wires.

The coating regulator, best shown in Figures '7, 8 and 9, may comprise a cross beam 25 in which is splined a bar 26 having in its upper edge a plurality of V-notches transversely convex, one for each of the wires leaving the bath. The notched bar is inclined slightly so as to lie transversely of the wires emerging from the bath. Co-a'cting with each of the notches of thebar is a blade 27 slidably held within guides 28 and 29-carried by a lever 30 which is pivotally mounted on'a shaft 31'extending transversely above the beam 25 and parallel therewith. Each lever may be equipped adjacent its fulcrum with a yoke-shaped bearing 32 adapted to fit over the shaft whereon it is held with the aid of a gravity pin 33. By pulling this pin out, the lever, together with its associated blade, may be demofunted from the shaft. Joined to the upperend of the lever is a tension spring '34 which extends over to a cross frame member 35 for connection therewith.

Associated with each blade is a pressure'device which may take the form of a weighted arm 40 pivoted at .41 to a bracket which extends rearwardly from the upper guide 29. Rested upon the upper end of the blade 27 is the arm 40 whose weight is adjustable to vary the pressure imposed upon the blade by which it is maintained in 9.

- downward positibn with a desired tension.

required, as when a wire joint encounters the coating regulator. 'When this happens, some of the excess coating material m previously scraped from the wire is released for discharge upon the forward side of the beam which is provided with a slanting surface 43 along which such material may freely slide down into the bathor elsewhere, as desired.

Each blade notch co-operates with a notch in the bar 26 to provide a small opening through which the wire may pass. The size of these openings may be easily adjusted in accordance with the diameters of the wires to be treated. Thus, with thirty wires, more or less, traveling through the galvanizing bath at one time, there may be a dozen ormore diflerent sizes, but the otherwise secured fixedly in place and may advantageously be formed of Stellite which is an alloy combining cobalt, chromium and tungsten in substantial parts together with small amounts of iron, sulphur, phosphorous, etc., or other hard material which is resistant to wear and corrosion by molten zinc. In practice, the V-notchesso reinforced by hardened inserts will function without appreciable wear over a prolonged period of service.

Coming now to the flame apparatus, I have shown a supporting framework S on which is carried upper and lower deflector surfaces with open spaces around on all four sides. As best shown in Figures 1, 2 and 3, the lower deflector surface may comprise a lining 50 of flame deflector blocks supported on bars 51 mounted upon the framework. Along the sides of the lower deflector surface and across the end-thereof proximate to the galvanizing bath, a low wall 52 is desirably provided, as shown.

The upper deflector surface includes a plurality distance suilicient to accommodate the wires entering the flame apparatus, with proper allowance for whipping and vibration incident to their travel. To mount the several flame projector blocks in place, I may utilize an angle bar 60 extended transversely across the apparatus with its end supported by the framework, and a series of clips 61, each having its upper end connected to the angle bar and its lower end laterally turned to engage within a notch 62 formed in the rear .wall of the flame projector block. To support the forward ends of the flame projector blocks, I use a transversely extending bar 63 here shown as a hollow tube having its ends suitably connected to the framework, the tube lyingwithin a notch 64 formed in the forward face of flame projector block. A cooling medium, such as water, may be circulated through the tube in case it is found desirable.

Referring particularly to Fig. 3, each flame projector block is socketed inwardly at 65 from its upper face to receive one end of a tube 66 closed at its bottom except for an angularly directed hole 67 in communication with the inner end of a passage 68 which opens upon the under face of the flame projector block. This passage is angularly disposed with respect to the direction of wire travel, so that a flame issuing therefrom will be projected downwardly in a forward direction for rebound again and again between the lower and upper deflector surfaces throughout the length of the apparatus. From the tube 66, suitprojected for repeated rebound between the lower and upper deflector surfaces throughout the length of the apparatus in the manner already indicated.

The remainder of the upper deflector surface is made of likedeflector blocks in adjacent relation, and in number and extent sufllcient to overlie substantially the entire area of the lower deflector surface. The rearmost row of upper deflector blocks, as shown, abuts the forward face of the flame projector blocks. The front row of upper deflector blocks terminate about even with the corresponding end of the lower deflector surface, and the sides of the upper deflector surface formd by the outermost rows of blocks extending lengthwise of the apparatus terminate,

- by reference, slightly inside of the low walls 52 upstanding adjacent the edges of the lower deflector surface. According to my invention, ad-

'jusiment may be made to provide for a gradual decrease of the intervening space toward the exit end of the apparatus. In this manner, the space between the upper and lower deflector surfaces, while remaining open on all sides, is narrowed slightly toward the exit end. The flames operating upon the wires during their travel through the apparatus issue from the rear end forwardly in an angular direction for repeated'rebound through a space which may gradually decrease toward th exit end of the flame apparatus. The upper deflector blocks which are of suitable refractorymaterial may be notched at on-opp,osite sides (see Figure 5) to provide shoulders with which engage clips 86 that extend upwardly for adjustable clamping connection with supporting bars 8.7 running longitudinally of the apparatus. Each supporting bar is adjustably sustained near its rearward end, as by means of a'djustably to a transverse angle bar 89. Sustaining the forward end of each supporting bar is a transverse angle bar 90 from which are upwardly extended bolts 91 having their threaded ends adjustably carried by a transverse angle bar-92. By

proper manipulation of the several clips 86, each upper deflector ,block may be individually ad: justed, and by adjustment of the several bolts .88 and 91,. I provide for raising or lowering of the supporting'bars separately or together at either or both ends, with consequent vertical movement of all the flame deflector blocks carried thereby. This is a highly desirable feature as it enables between them alleys each slve temperatures.

guided from the coating regulator through the flame apparatus and .to a point therebeyond until the treated coating is sufliciently set to with- Stand exte'rior frictional contact. The travel of the wires is produced, as is common practice, by suitable take-up mechanism (not shown) so that the wires are under constant tension. The design of the flame apparatus, as well as its relation to the adjacent units, should be such that "it will, not contact with any wire, even where it sags the lowest. If necessary, the longitudinal contour of the upper and lower flame deflector surfaces may be slightly curved, as required, to conform to any sag which the wires may take. To properly guide and sustain the wires in relation to the vertically narrow confines of the flame apparatus I provide, at a point of several feet beyond its exit end, a guide G consisting of a series of vertically adjustable grooved ball-bearing rollers 95, one for each wire, and all mounted, if desired, upon a common framework 96. Each roller bears. lightly against the under side of the wire so as not to disturb the coating which at that point may still be somewhat soft. The contact of these rollers with the wires is sufficient, however, to prevent undue vibration or whipping, with consequent disturbance of the coating in process of being redistributed, smoothed, and evened by the treatment applied in the flame apparatus.

It is feasible to utilize various forms of apparatus for carrying out this invention. The'one already described is admirably suited to meet all requirements, as I have demonstrated in prac-: 1 5 tice. 'As suggestive of certain modifications which may optionally be used, I have shown in Figure 10 a construction having a lower deflector surface over which is arranged a plurality of spaced vertical refractory walls 100, forming adapted for the reception of a wire. Extending longitudinally within each alley is. a fuel pipe 101 mounting a plurality of angularly directed burners 102 adapted to project' flames against the wire which lieaproximate to one wall. In thiscase, the flames will strike against one side of the wire and pass beyond to bound off of the adjacent wall, down to the deflector surface and thence back, the resulting effect being if' desired. a hook bolt 88 having its threaded end secured 'A further modification is suggested in Fig. 11, .whereinl have shown a series of flame deflector blocks 110 having opposite faces 111 concave in a direction lengthwise of the apparatus. Between Y travel between the burners and the confronting v row of blocks. In the construction shown, the fuel line is jacketed at 113, permitting the use'of a cooling medium to prevent attainment of exces- In this form of apparatus the flames playing upon the wires rebound upon con- 15;

tact with the concave faces of the blocks was to impinge upon the wire side opposite the burners, to assure a proper treating action at all points. The blocks may be adjustably carried upon bolts 114 hooked over supporting bars 115 in the manner shown. Upper and lower deflector surfaces may optionally be employed with this construction.

In Figs. 12 and 13, I have shown a further modiflcation in which the wires travel, desirably in groups of two over a lower deflector surface, with a row of blocks 120, concave on their under faces providing a longitudinal archway over a single group of wires, asshown. These blocks may be supported adjustably by clips 121 which connect with supporting bars 122 adjustably supported at opposite ends if desired. Over each row of flame deflector blocks is a fuel conduit 123 from which depend nozzles 124 extending angularly in a forward direction. Each nozzle is fitted within the upper end of an angularly disposed socket 125 which opens out upon the lower face of the block. In this manner, I provide for the issuance of flames from the under face of the blocks, one behind the other in a row, and projected forwardly upon a lower deflector surface so as to rebound for impingement upon the wire side opposite .to the flame deflector blocks above. This construction difiers from the others principally in that a series of flames projecting angularly in a single row from the center of an archway impinge upon a plurality of wires traveling therebelow within the confines thereof so as to receive'treatment throughout the length of their travel within the flame apparatus. I

According to this invention, I include (1) maintenance of proper fluidity of the coating bath through a close control of temperature; to within,

say, plus or minus 5 Fahrenheit; (2) removal of excess coating from the wire as it emerges from the bath so as to leave on the wire only so much coating as may be redistributed, smoothed, and evened by the flame action;- (3) regulable impingement of the coating by flames acting upon every portion of the wire surface through an extended treating zone and for a time interval suflicient to accomplish this result; and (4) guidance of each wire throughout the zone of flame treatment and for a distance therebeyond to safeguard against contact with proximate parts. By maintaining the temperature of the zinc bath close to a temperature which is found suitable, the

.fiuidity, of the coating adhering to the wire will be substantially uniform. The skimmings, foreign matter, and coating material carried out of the bath in excess of that which the flames will even and smooth, are takenoif by the regulator, and. with each opening of the notched blades, occasioned periodically by passage of joints and/or accumulated skimmings, such removed material is automatically released and the coating regulator cleared. This is important, because the accumulation of dross and sklmmingsxby the regulator affects somewhat the amount of coating remaining on the wire when coming into the zone of flame treatment. 'By maintaining uniform viscosity of the molten bath. variation in the amountof coating, i. e., the weight-per unit area of wire surface, is held to a minimum.

Heretofore there has been considerable variation in.the amount of coating left on the wire after leaving a V-notched bar, resulting in the finished product having one characteristic for, say, one

thousand feet or more and another different characterlstic for a succeeding one thousand feet or about .068" diameter.

more. All such variable factors are removed by the means and process set forth herein which has many advantages from a commercial standpoint. The wire may be perfectly treated when advanced at a; fairly rapid speed depending upon its gauge and the consequent amount of coating which it may carry. The resulting coating is found to be more uniformly distributed over and around the wire surface, as determined by a copper sulphate test.

For closely controlling the temperature of the bath which is desirably insulated to prevent loss of heat by radiation, some such apparatus may be used as is represented diagrammatically in Fig. 2. Here I have shown heating devices in the form of burners 130' receiving liquid or gaseous fuel from supply pipes 131 equipped with regulating valves operable by means 132 electrically energized through actuation of a control 133 which is responsive to temperature conditions in the bath, the operation being automatic at all times so asto maintain the bath at approximately the temperature for which the control instrument is set. The clearance of each coating regulator is also adjustable to accord with the diameter of 100 the wire passing therethrough, and once a setpo'rtant, viz., the bath temperature, being usually quite variable. By maintaining a close control over the temperature of the molten bath, a sub- 'stantially uniform weight of coating per unit of surface area is carried out by the wire, making possible thereafter by means of the regulator to limit the weight of such coating to a point at which the action by flames impinging upon every portion of the wire surface will perform a uni- 1 5 form redistribution (as necessary), and smoothing of all the remaining coating.

As a specific example of theapplication of this process to the galvanizing of wires, I have passed a wire of 12 gauge (.0985" diameter) through a molten zinc coating bath of approximately 860 F. for a distance of fifteen feet. Immediately upon leaving the coating bath the wire was acted upon by the regulator the opening of which was maintained at approximatedly. .002" larger than the diameter of the wire. The wire was travv eling continuously at a speed of 107 feet per minute. The weight of the coating was approximately .48 ouncesper square foot of wire surface. .The copper sulphate test was four minutes at the first failure, and five and one-half minutes for complete failure. Inanother case I have treated similarly an 11 gauge wire *;(.1205" diameter) which moved at a speed of 90 feetper minute acquiring in its travel a coating which weighed '135 approximately flu-ounces per square foot of wire surface. When subjected to,the copper sulphate 'test, first failure of the wire was four minutes,

and complete failure at five and one-half minutes; The flame for smoothing the wire was exactly the same in both cases. By varying the flame, instead of the speed of wire travel, the same results are obtainable within certain practical limits.

In the above cases I used manufactured gas, pressure about 7 pounds, which was passed 145 through an air inspirator, having a gas opening of By means of regulating valves for the gas and air, the flame may be maintained at a point suitable for uniform dis- 'tribution and smoothing of the coating upon the 5 flame action, which follows immediately upon delimiting of the weight of coating applied to each wire, accomplishes the dual purposes of (1) maintaining the coating in'a molten condition while (2) redistributing every portion of the coating, as necessary, to assure its even and smooth spread over the wire surface.

A freshly applied molten coating, which is regulated as to amoimt and then subjected to the action of a flame in the manner above described, is thereby distributed evenly over and around the surface of the body, and its own surface is also smoothed. Such a treatment comprises, in effect, two steps, 1112., (1) regulation of the amount of coating and .(2) evening and smoothing of the coating finally remaining on the wire. So far as concerns the attainment of evenness and smoothness, the treated coating of my invention may be compared with wiped coatings as heretofore produced by a single step process without the use of a flame; but the resuitsv according to my process are superior, the coating may be more closely regulated as to amount, the coating flnally remaining on-the wire is evened and smoothed more uniformly and perfectly, and the operations which produce these results are performed with greater speed and certainty. A coating which is wiped by theapparatus and process of my invention will conform to very exacting specifications such as are com -monly established for wires in particular.

. ment.

gested, a number of coated bodies, such as wires (round, flat, etc.) may travel along in parallelism continuously in a linear direction to be simultaneously treated. The flame apparatus is desirably heat-insulated, top and bottom, and may operate with any selected number of flames, depending upon the number of wires or other bodies passing through the apparatus. In case it is desired to operate the apparatus at reduced capacity, then it becomes unnecessary to employ flames in the unused part of the apparatus, thus expense of op- I claim: 7

1. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal iii-which is comprised opposed coacting deflector surfaces adjacent which the coated body is moved, and means fo projecting a flame angularly from one of said surfaces toward another -surface for repeated rebound from one surface to another to produce a flame impingement upon the molten coating with consequent uniform distribution and smoothing thereof.

2. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal in, which is comprised opposed deflector surfaces deflning between them a space open on all sides and narrowing toward one end, .means for moving the coated body free of contact with the deflector surfaces through the space between them toward the narrower end, and means for projecting a flame from one surface angularlytoward the other for repeated rebound between the two surfaces whereby to produce a flame impingement upon the molten coating with consequent uniform distribution and smoothing thereof.

3. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal in which is comprised opposed deflector surfaces defining between them a space which is open at opposite edges, means for projecting a flame from one surface angularly toward the other for repeated rebound between the two surfaces in a direction toward one of the open edges whereby to produce a flame impingement upon the molten coating of the body passing between said surfaces away from the flame, and means for adjusting one surface relative to the other 0 whereby to vary the space therebetween.

the distance between two opposite edges thereof,

and means for adjusting selected portions of one flame deflector surface toward or from the other whereby to vary the clearance at points there- In the various forms of apparatus herein sugbetween; t

5. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal in which 'is comprised upper and lower deflector surfaces in opposed relation defining between them a narrow space open at the edges of the two surfaces, the upper deflector surface comprising aplurality of independently adjustable deflector blocks movable toward and from the lower deflector surface, vertically adjustable means supporting a plurality of blocks comprised in the upper deflector surface adapted to raise and lower such blocks in unison, and means for projecting a flame from one surfaceangularly.

toward the other for repeated rebound between the two surfaces for a substantial distance throughout the space therebetweeii.

6. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal in which is comprised a transversely arched deflector surface extending lpngitudinally of the movement of the body, and means for projecting .a flame toward the, deflector surface for rebound therefrom longitudinally of the archway whereby to impinge upon various circumferential portions of the surface of a moltencoating freshly applied to a body passing between the archway and the flame projecting means. I v

7. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal in which is comprised a deflector surface made up of a plurality of independently adjustable deflector blocks movable in parallelism into and out of a common plane whereby to change the position of such plane or any selected part thereof, and means for projecting a flame for rebound stantial portion of. its

8. An apparatus for continuous flame-treating of a metallic body freshly coated with molten metal in whichis comprised a deflector surface made up of a plurality of independently adjustable deflector blocks movable into and out of a common plane, adjustablemeans supporting a plurality of the deflector blocks adapted to move the same in unison into or out of a plane common of the molten coating to uniformly distribute and smooth said coating without removing any of the coating remaining upon the body.

10. In combination with a molten galvanizing bath, a coating regulator in which is comprised co-acting parts having opposed surfaces in offset relation adapted to remove a selected amount of molten coating from a metallic body which is passed between such surfaces, and a fixed single pivotal support forone of said parts permitting it to yield away from the other in the direction of body movement in response to an enlargement carried by the body, and means to even. and

smooth the remaining coating upon the body.

without removal of coating therefrom.

11. In combination with a molten galvanizing bath adapted to apply a molten coating to a wire traveling therethrough, a coating regulator in proximity to the bath comprising ,two parts having opposed V notches between which the wire is passed, a single fixed pivotal support for one of said parts, and means for maintaining the notched faces ina predetermined spaced relation close to the wire surface whereby a regulated amount of molten coating is removed from the wire while passing therethrough, and means to even and smooth the remaining coating upon the wire without removal of coating therefrom.

12. In combination with a molten galvanizing bath adapted to apply a coating to a wire traveling therethrough, a coating regulator in proximity to the bath comprising automatically adjustable parts having opposed notches closely fitting over the wire, and a fixed single pivotal mounting for one of the said parts permitting its separation from the other when required for passage of an enlargement therethrough, and means to even and smooth the remaining coating upon the wire without removal of coating theresmooth the remaining coating upon the wire withfrom.

13. In combination with a molten galvanizing bath adapted to apply a coating'to a wiretraveling therethrough, a coating regulator in proximity to the bath comprising automatically adjustable parts formed with opposed notches closely fitting over the wire, one of said partslying in offset but adjacent relation to the other, and means providinga single fixed pivotal support for one part permitting it to move away from the other when required for passage of an enlargement therethrough, and means .to even and out removal of coating therefrom.

14. In combination with a molten galvanizing bath adapted to apply a'coating to a wire traveling therethrough, a coating regulator inproximity to the bath comprising two parts having opposedvnotchesfacedwithmaterialresistant to wear and corrosion by molten zinc between which facing material the wire is passed for removal of excess moltencoating applied to the wire.

15. In combination with a molten galvanizing bath, a flame-treating apparatus'having opposed deflector surfaces narrowly spaced and open at opposite ends adapted toreceive between them a wire traveling from the bath with applied coating still in molten condition, means for directing from the deflector surfaces a flame which impinges upon opposite sides of the wire, and means for guiding the wire within the space defined by the opposed deflector surfaces free of contact with such surfaces.

16. In combination with a molten galvanizing bath, means for regulating the coating applied to a metallic body emerging from the bath, comprising two cooperating ofiset parts, one fixed and the other yieldable in the direction of body travel, adapted to remove from opposite surfaces of the body al coating in excess of that finally to remain thereupon, and means to even and smooth the remaining coating, upon every portion of the surface of the body. 1

17. In combination with a molten galvanizing bath, a flame treating apparatus in which is included an adjustable flame deflector surface and flame projector means both positioned adjacent a wire traveling from the bath with applied coating still in molten condition, and means adjustable relative to the' flame deflector surface and movable into light contact with the wire for reducing whipping and vibration of the wire adjacent'such flame deflector surface and flame projector means.

18. The process of galvanizing a metallic body which comprises the successive steps continuously performed of coating the body with a molten metal, removing from the body all molten metal in excessof that finally to remain thereupon,

through a molten metallic bath whose fluidity is closely controlled at approximately plus or, minus flve degrees of the bath temperature, removing from the wire all molten metal in excess of-that finally to remain thereupon, and flame-treating the coated wire to' effect a uniformdistribution and smoothing of the remaining coating upon every portion of the surface of the wire.

20. The process of galvanizing wire which comprises the successive steps continuously performed of coating the wire by advancing the same through a molten metallic bath in which the wire acquires a coating, regulating the amount of coating to remain upon the wire, and flame-treating'the regulated coating without the removal of coating from the wire to e'fl'ect a uniform distribution and smoothing of the coating upon every portion of the surface of the wire.

wire which comprises-the steps of drawing a wire through a molten coating bath and closely controlling the ..bath temperature at a desired point to render-,the applied coating of uniform fluidity, regulating the amount of coating upon the wire to a desired weight per unit of surface area in accordance with the fluidity of the applied coating, and in subjecting the coated wire so treated to the action of a flame applied for a time interval sufficient to evenly distribute and smooth all the remaining coating over every portion of the wire surface.

22. In the art of continuously galvanizing wire which comprises means for coating and wiping the wire including a molten coating bath, a coating regulator, and a flame,means to closely control the bath temperature at a desired point to render the applied coating of uniform fluidity, means to adjust the coating regulator in accordance with the fluidity of the applied coating,

whereby to reduce the coating to a desired amount and weight per unit of surface area, and means to cause the flame to act upon the regulated coating upon the wire for a time interval sufficient to evenly distribute and smooth all the remaining coating over every portion of the wire surface.

23. The process of continuously galvanizing wire which comprises the steps of advancing a wire through a molten coating bath of controlled temperature, regulating the applied coating as required by its fluidity to reduce the coating to a desired amount and weight per unit of surface area, applying a flame over a material extent of regulated coating upon the wire, and in so coordinating the steps of coating regulation and flame application that the molten coating applied to the wire is reduced in amount and weight to a point at which the flame will evenly distribute and smooth all the remaining molten coating over every portion of thewire surface.

24. In the art of continuously galvanizing wire,

a molten coating bath, means to draw the wire through the coating bath, a coating regulator, means to adjust the regulator in accordance with the fluidity of the applied coating to reduce such coating to a desired amount and weight-per unit of surface area, and means to apply a flame in regulable extent upon the reduced coating of the wire, the regulator adjustment and flame application being so co-ordinated that the molten coating applied to the wire is reduced by the regulator in amount and weight to a point at which the flame will evenly distribute and smooth all the remaining molten coating over every portion of the wire surface. 4

25.The process of galvanizing wire which comprises the successive steps of coating a wire with a molten' metal, removing molten coating from the wire to reduce the coating to a desired amount and weight per unit of surface area, and flametreating the coated wire without the removal of any of the coating therefrom to evenly distribute and smooth the remaining coating over every portion of the wire surface.

26. The process of galvanizing wire which comprises passing a wire through a molten metallic bath in a linear direction, directinga flame upon one side of the coated wire so as to extend beyond the other side of the wire, and repeatedly redirecting the flame travel from opposite sides of the wire for repeated impingement upon every portion of the molten coating for a material extent in the direction of travel of the wire.

JULIAN L. SCHUELER. 